Specification

Technical specification

Pot life (200g, 25°C)

    Hours

        > 5 hours

Cure Time (200g, 25°C)

     Hours

      48

Full Cure (25°C)

     Days

       7

Recommended Casting Thickness

      mm

        5 - 35

  

Resin

Hardener

Colour

Transparent liquid

Transparent liquid

Specific gravity

1.10g/cm3

1.08g/cm3

Viscosity at 25 deg C

500-900cps

320-500cps

Strength Paramaters

PARAMETER TESTED

ProCast Max

ProCast Max

Hardening time

7 days at room temp
6 hours At 80 ° C
Strength
for bending, [MPa]
PN-EN ISO 178: 2006
66,60

 

72.60

 

Modulus of elasticity
when bending, [MPa]
PN-EN ISO 178: 2006
2,380.00

 

2,480.00

 

Deflection arrow, [mm]
PN-EN ISO 178: 2006
6.50

 

7.10

 

Breaking stress, [MPa]
PN-EN ISO 527-1: 1998
PN-EN ISO 527-2: 1998
28,60

 

35.50

 

Modulus of elasticity
when stretching, [MPa]
PN-EN ISO 527-1: 1998
PN-EN ISO 527-2: 1998
2,450.00

 

2,490.00

 

Strength
for compression, [MPa]
PN-EN ISO 604: 2006
63.70

 

64.20

 

Impact resistance without notch, [kJ / m2]
PN-EN ISO 179-1: 2004
66.00

 

69.00

 

Hardness method
Barcola, [° B]
ASTM-D 2583-07
5.00

 

16.00

 

Hardness method
pressing the ball, [MPa]
PN-EN ISO 2039-1: 2002
105.00

 

106.00

 

Temperature of deflection
according to Martens, [° C]
PN-90 / C-89025: 1990
43,00

 

47,00

 

Temp. deflections under HDT load, [° C]
44,00

 

48,00
CHEMICAL RESISTANCE :
AGGRESSIVE ENVIRONMENT
ProCast Max
EXPOSURE TIME
1 month
Supply water
+
Sodium hydroxide 10 - 45%
+
Hydrochloric acid 10%
+
Concentrated hydrochloric acid
-
Sulfuric acid 20%
-
Phosphoric acid 10%
0
Nitric acid 10%
+
Acetic acid 5%
+
Citric acid 10%
+
Sodium carbonate 10%
+
Kitchen salt 20%
+
Ethanol 45%
+
Ethanol 96%
0
Toluene
-
Xylene
-
Acetone
-
Petrol
+
Diesel
+
Perhydrol 3%
+
Ethyl acetate
-
Ammonia 10%
+